15kg 1.2mm LP-G Hardfacing Flux Core Mig Wire
$579.00
Product Introduction
Welding Alloys LP-G is an all-positional flux core mig wire for hardfacing, ideal for metal-metal wear and high abrasion in agricultural, earthmoving, and recycling machinery. Provides medium alloy martensitic steel deposit with 55-60 HRC hardness and good impact resistance.
Product Parameters
| Wire Diameter | 1.2mm |
| Spool Weight | 15kg |
| Hardness (3 layers) | 55-60 HRC |
| Shielding Gas | Argon 5/2 or similar |
| Polarity | DC+ |
15kg – 1.2mm Welding Alloys LP-G Hardfacing Flux Core Mig Wire for Positional Welding
Unlock superior wear resistance for your heavy-duty machinery with Welding Alloys LP-G Hardfacing Flux Core Mig Wire. Engineered for all-positional welding, this 1.2mm wire delivers exceptional metal-metal wear protection, making it ideal for ground-engaging applications. Whether you’re working on agricultural equipment, earthmoving machinery, or recycling tools, this flux-cored wire ensures durable, high-hardness deposits that stand up to extreme abrasion and impact.
Especificaciones básicas
| 1.2mm | |
| Spool Weight | |
| Hardness (3 layers) | 55-60 HRC |
| Martensitic Steel | |
| Shielding Gas | Argon 5/2 or similar mixed gas |
| 100-280A (Optimum: 220A) | |
| Voltage Range | 18-30V (Optimum: 22V) |
| Polarity | DC+ |
| AS/NZS 2576-2005, DIN 8555, EN 14700 |
Ventajas clave
All-Positional Versatility: Vertical welding capability allows hardfacing in complex applications, eliminating position limitations.
Extreme Hardness: 55-60 HRC weld deposits resist abrasion in dry/wet environments, outperforming standard wires.
Cost-Effective: Economical solution with superior wear resistance, reducing maintenance and replacement costs.
Impact Resistance: Medium alloy composition balances hardness with toughness for heavy-duty use.
Aplicaciones
Ideal for agricultural & earthmoving equipment, compactor wheels, shredders, bucket teeth, cutting edges, steel mill rolls, conveyor chutes, and wear liners. Perfect for site welding to protect corner joints and exposed seams.
Pruebas de Rendimiento
Field-tested in mining, construction, and recycling industries, LP-G wire consistently delivers 30% longer service life compared to conventional hardfacing wires. Machinable with special tools for post-weld finishing.
Aseguramiento de Calidad
Manufactured to global standards (AS/NZS 2576-2005, DIN 8555, EN 14700) and equivalent to Stoody 965-G. Each spool undergoes rigorous quality checks to ensure consistent performance.
Why Choose LP-G?
Unlike solid wires, LP-G’s flux core enhances weld integrity and positional flexibility. Its Martensitic steel composition offers a unique blend of hardness and impact resistance, making it the top choice for demanding wear applications.
Preguntas Frecuentes
Q: Can LP-G be used with pure CO2 gas?
A: No, optimal results require Argon 5/2 or similar mixed gas.
Q: Is preheating required?
A: Preheating is recommended for thick sections to prevent cracking.
Q: What is the shelf life?
A: 2 years when stored in dry, cool conditions.
Ready to enhance your equipment’s durability? Contact us today for bulk pricing, technical support, or sample requests. Our team of welding experts is here to help you optimize your hardfacing process.